Optical fiber with chromatic dispersion compensation in the S band

ABSTRACT

The invention relates to the field of optical fibers for wavelength division multiplex transmission networks. It provides an optical fiber with chromatic dispersion compensation in the S band from 1 460 nm to 1 530 nm having a negative chromatic dispersion at the wavelength of 1 495 nm and at least three core slices, preferably at least four core slices. The single core slice or the first core slice is very deeply buried and preferably has as at the wavelength of 1 495 nm a chromatic dispersion to dispersion slope ratio whose absolute value is from 68 nm to 158 nm.

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application is based on French Patent Application No. 02 16 616 filed Dec. 24, 2002, the disclosure of which is hereby incorporated by reference thereto in its entirety, and the priority of which is hereby claimed under 35 U.S.C. §119.

BACKGROUND OF THE INVENTION

[0002] 1. Field of the Invention

[0003] The invention relates to the field of optical fibers for wavelength division multiplex transmission networks.

[0004] 2. Description of the Prior Art

[0005] Increasing information bit rates on this type of network impose compensation of chromatic dispersion and dispersion slope over bands of the spectrum other than the C band. The S band extends approximately from 1 460 nm to 1 530 nm. The C band extends approximately from 1 530 nm to 1 565 nm. The L band extends approximately from 1 565 nm to 1 625 nm. The U band extends approximately from 1 625 nm to 1 675 nm. The most widely used band is the C band. The invention relates to fibers with chromatic dispersion compensation in the S band.

[0006] In the prior art, it is known to combine certain types of dispersion shifted optical fibers reducing crossed non-linear effects, known as non-zero dispersion shifted fiber (NZ-DSF), with dispersion compensating fiber (DCF), thereby achieving a transmission line with no dispersion over a wide spectral range.

[0007] The patent application EP 1219986 discloses using an optical fiber with chromatic dispersion compensation in the S band, but the examples described with two or three slices either have a ratio between the attenuation at 1 520 nm and at 1 500 nm greater than two or a chromatic dispersion to dispersion slope ratio that renders them unsuited to the object of the invention.

[0008] The invention proposes a chromatic dispersion compensating optical fiber which, either because of profiles with at least four slices or because of profiles with three slices having structures corresponding to particular ranges of index and radius, provides effective compensation in the S band of the chromatic dispersion of a certain range of line optical fibers, combined with attenuations at 1 500 nm and at 1 520 nm that are comparable. A particularly advantageous aspect is the very deeply buried nature of the index of the first buried slice (or of the only buried slice if there is only one) relative to the index of the central slice.

SUMMARY OF THE INVENTION

[0009] The invention provides an optical fiber with compensation of chromatic dispersion in the S band from 1 460 nm to 1 530 nm, for use in wavelength division multiplex transmission networks, having a negative chromatic dispersion at the wavelength of 1 495 nm, comprising successively from the center toward the periphery a core having a varying index profile and then a cladding of constant index, said varying index profile of said core comprising successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a buried slice having a minimum index lower than the index of said cladding, and an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, the difference Δn₁ between said maximum index of said central slice and the index of said cladding being from 11.5×10⁻³ to 20.0×10⁻³, the radius r₁ of the portion of said central slice having an index higher than the index of said cladding being from 1.6 μm to 2.6 μm, the value S₀₁ of the integral ∫₀^(r1)Δ  n(r) ⋅ r

[0010] between a zero radius and the radius of the portion of said central slice having an index higher than the index of said cladding of the index difference relative to said cladding being from 28×10⁻³ μm to 34×10⁻³ μm, and the radii and the indices of each of said slices being determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to dispersion slope ratio whose absolute value is from 68 nm to 158 nm.

[0011] The radii and the indices of each slice are preferably determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 80 nm to 118 nm. The radii and the indices of each slice are advantageously determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 87 nm to 105 nm.

[0012] The invention also provides an optical fiber with compensation of chromatic dispersion in the S band from 1 460 nm to 1 530 nm, for use in wavelength division multiplex transmission networks, having a negative chromatic dispersion at the wavelength of 1 495 nm, comprising successively from the center toward the periphery a core having a varying index profile and then a cladding of constant index, said varying index profile of said core comprising successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a first buried slice having a minimum index lower than the index of said cladding, an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, a second buried slice having a minimum index lower than the index of said cladding, the radii and the indices of each of said slices being determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 68 nm to 158 nm.

[0013] The radii and the indices of each slice are preferably determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 80 nm to 118 nm. The radii and the indices of each slice are advantageously determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope whose absolute value is from 87 nm to 105 nm.

[0014] The invention further provides an optical fiber with compensation of chromatic dispersion in the S band from 1 460 nm to 1 530 nm, for use in wavelength division multiplex transmission networks, having a negative chromatic dispersion at the wavelength of 1 495 nm, comprising successively from the center toward the periphery a core having a varying index profile and then a cladding of constant index, said varying index profile of said core comprising successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a buried slice having a minimum index lower than the index of said cladding, and an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, the absolute value of the minimum index of said buried slice being greater than or equal to 60% of the absolute value of the maximum index of said central slice. The depth to which is buried this slice that is very deeply buried relative to the height of the central slice is an important advantageous feature that facilitates obtaining good compensation in the S band not only of chromatic dispersion but also of dispersion slope, without significantly degrading the other properties of the chromatic dispersion compensating optical fiber. The absolute value of the minimum index of said buried slice is preferably greater than or equal to 90% of the absolute value of the maximum index of said central slice.

[0015] Other advantageous features with the same aim are described next.

[0016] The varying index profile of said core preferably comprises successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a first buried slice having a minimum index lower than the index of said cladding, an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, and a second buried slice having an index lower than the index of said cladding. This is therefore an index profile comprising at least four slices.

[0017] The radii and the indices of each slice are preferably determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 68 nm to 158 nm.

[0018] The dispersion compensating optical fiber according to the invention is associated with a line optical fiber in an optical fiber transmission system. In one embodiment, the optical fiber transmission system comprises the combination of a line optical fiber and an in-line dispersion compensating optical fiber according to the invention. In another embodiment the optical fiber transmission system comprises the combination of a line optical fiber and an in-module dispersion compensating optical fiber according to the invention.

[0019] In a first preferred embodiment of the invention, the chromatic dispersion compensating optical fiber according to the invention comprises a type of varying core index profile with three slices. This type of core varying index profile comprises successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a buried slice having a minimum index lower than the index of said cladding, and an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice. The central slice is preferably rectangular but can also be trapezium-shaped, triangular or alpha-shaped for example. The other slices are preferably rectangular but can also be trapezium-shaped, triangle or alpha-shaped, for example.

[0020] A certain number of ranges or of preferred relations, in particular for the indices and the radii of the type of core index profile with three slices are described next that improve the quality of chromatic dispersion compensation in the S band of the line optical fiber and the other properties of the chromatic dispersion compensating optical fiber according to the invention.

[0021] The value T₀₁ of twice the integral ∫₀^(r1)Δ  n(r) ⋅ r ⋅ r

[0022] between a zero radius and the radius r₁ of the portion of said central slice having an index higher than the index of said cladding of the product of the index difference relative to the cladding and the radius is preferably from 51×10⁻³ μm² to 79×10⁻³ μm².

[0023] The difference Δn₂ between the minimum index of said buried slice and the index of said cladding is preferably from −10×10⁻³ to −7.0×10⁻³ and the outside radius r₂ of said buried slice is from 4.5 μm to 6.5 μm.

[0024] The value S₁₂ of the integral ∫_(r1)^(r2)Δ  n(r) ⋅ r

[0025] between the radius r₁ of the portion of said central slice having an index higher than the index of said cladding and the radius r₂ of the portion of said buried slice having an index lower than the index of said cladding of the index difference relative to said cladding is preferably from −42×10⁻³ to −22×10⁻³ μm.

[0026] The value T₁₂ of twice the integral ∫_(r1)^(r2)Δ  n(r) ⋅ r ⋅ r

[0027] between the radius r₁ of the portion of said central slice having an index higher than the index of said cladding and the radius r₂ of the portion of said buried slice having an index lower than the index of said cladding of the product of the radius by the index difference relative to said cladding is preferably from −350×10⁻³ to −160×10⁻³ μm².

[0028] The difference between the maximum index of said annular slice and the index of said cladding is preferably from 1.0×10⁻³ to 8.0×10⁻³ and the outside radius of said annular slice is preferably from 7.3 μm to 10.2 μm.

[0029] The value S₂₃ of the integral ∫_(r2)^(r3)Δ  n(r) ⋅ r

[0030] between the radius r₂ of the portion of said buried slice having an index lower than the index of said cladding and the radius r₃ of the portion of said annular slice having an index higher than the index of said cladding of the index difference relative to said cladding is preferably from 5×10⁻³ to 15×10⁻³ μm.

[0031] The value T₂₃ of twice the integral ∫_(r2)^(r3)Δ  n(r) ⋅ r ⋅ r

[0032] between the radius r₂ of the portion of said buried slice having an index lower than the index of said cladding and the radius r₃ of the portion of said annular slice having an index higher than the index of said cladding of the product of the radius by the index difference relative to said cladding is preferably from 70×10⁻³ to 207×10⁻³ μm².

[0033] The value S₀₃ of the integral ∫₀^(r3)Δ  n(r) ⋅ r

[0034] between a zero radius and the radius r₃ of the portion of said annular slice having an index higher than the index of said cladding of the index difference relative to said cladding is preferably from 2.8×10⁻³ to 18.2×10⁻³ μm.

[0035] The value T₀₃ of twice the integral ∫₀^(r3)Δ  n(r) ⋅ r ⋅ r

[0036] between a zero radius and the radius r₃ of the portion of said annular slice having an index higher than the index of said cladding of the product of the radius by the index difference relative to said cladding is preferably from −108×10⁻³ to 57×10⁻³ μm².

[0037] The value U₀₃ of twice the integral $\int_{0}^{r3}{\Delta \quad {{n(r)} \cdot {\exp \left( \frac{- r^{2}}{a^{2}} \right)} \cdot r \cdot {r}}}$

[0038] between a zero radius and the radius r₃ of the portion of said annular slice having an index higher than the index of said cladding of the product of the radius and the index difference relative to the cladding and the function exp(−r²/a²) where a=1.58 μm is preferably from 24.4×10 ⁻to 28.5×10⁻³ μm².

[0039] In a second preferred embodiment of the invention, the chromatic dispersion compensating optical fiber according to the invention comprises a type of core varying index profile with four slices. The second type of core varying index profile comprises successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a first buried slice having a minimum index lower than the index of said cladding, an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, and a second buried slice having a maximum index lower than the index of the cladding. The central slice is preferably rectangular, but can also be trapezium-shaped, triangle or alpha-shaped. The other slices are preferably rectangular, but can also be trapezium-shaped, triangle or alpha-shaped, for example.

[0040] A certain number of ranges or of preferred relations, in particular for the indices and the radii of the type of core index profile with four slices are described next that improve the quality of chromatic dispersion compensation in the S band of the line optical fiber and the other properties of the chromatic dispersion compensating optical fiber according to the invention.

[0041] The difference Δn₁ between the maximum index of said annular slice and the index of said cladding is preferably from 12×10⁻³ to 20×10⁻³ and the radius of the portion of said central slice having an index higher than the index of said cladding is from 1.57 μm to 2.5 μm.

[0042] The value S₀₁ of the integral = ∫₀^(r1)Δ  n(r) ⋅ r

[0043] between a zero radius and the radius r₁ of the portion of said central slice having an index higher than the index of said cladding of the index difference relative to said cladding is preferably from 28.4×10⁻³ μm to 35.5×10⁻³ μm.

[0044] The value T₀₁ of twice the integral ∫₀^(r1)Δ  n(r)⋅  r ⋅ r

[0045] between a zero radius and the radius r₁ of the portion of said central slice having an index higher than the index of said cladding of the product of the index difference relative to the cladding and the radius is preferably from 49×10⁻³ μm² to 81×10⁻³ μm².

[0046] The difference between the minimum index of said first buried slice and the index of said cladding is from −12×10⁻³ to −5×10⁻³ and the outside radius of said first buried slice is preferably from 4.0 μm to 7.4 μm.

[0047] The value S₁₂ of the integral ∫_(r1)^(r2)Δ  n(r) ⋅ r

[0048] between the radius r₁ of the portion of said central slice having an index higher than the index of said cladding and the radius r₂ of the portion of said first buried slice having an index lower than the index of said cladding of the index difference relative to said cladding is preferably from −56×10⁻³ to −20×10⁻³ μm.

[0049] The value T₁₂ of twice the integral ∫_(r1)^(r2)Δ  n(r)⋅  r ⋅ r

[0050] between the radius r₁ of the portion of said central slice having an index higher than the index of said cladding and the radius r₂ of the portion of said first buried slice having an index lower than the index of said cladding of the product of the radius by the index difference relative to said cladding is preferably from −470×10⁻³ to −130×10⁻³ μm².

[0051] The difference (Δn3) between the maximum index of said annular slice and the index of said cladding is preferably from 1.0×10⁻³ to 8.0×10⁻³ and the outside radius of said annular slice is preferably from 6.8 μm to 12 μm.

[0052] The value S₂₃ of the integral ∫_(r2)^(r3)Δ  n(r) ⋅ r

[0053] between the radius r₂ of the portion of said first buried slice having an index lower than the index of said cladding and the radius r₃ of the portion of said annular slice having an index higher than the index of said cladding of the index difference relative to said cladding is preferably from 5×10⁻³ to 26×10⁻³ μm.

[0054] The value T₂₃ of twice the integral ∫_(r2)^(r3)Δ  n(r) ⋅ r ⋅ r

[0055] between the radius r₂ of the portion of said first buried slice having an index lower than the index of said cladding and the radius r₃ of the portion of said annular slice having an index higher than the index of said cladding of the product of the radius by the index difference relative to said cladding is preferably from 60×10⁻³ to 440×10⁻³ μm².

[0056] The difference Δn₄ between the minimum index of said second buried slice and the index of said cladding is preferably from −12×10⁻³ to 0 and the outside radius of said second buried slice is from 9 μm to 21 μm.

[0057] The value S₃₄ of the integral ∫_(r3)^(r4)Δ  n(r) ⋅ r

[0058] between the radius r₄ of the portion of said annular slice having an index higher than the index of said cladding and the radius of the portion of said second buried slice having an index lower than the index of said cladding of the index difference relative to said cladding is preferably from −153×10⁻³ μm to 0.

[0059] The value S₀₄ of the integral ∫₀^(r4)Δ  n(r)⋅  r

[0060] between a zero radius r₄ and the radius of the portion of said second buried slice having an index lower than the index of said cladding of the index difference relative to said cladding is preferably from −138×10⁻³ to 22×10⁻³ μm.

[0061] The value T₀₄ of twice the integral ∫₀^(r4)Δ  n(r)⋅  r ⋅ r

[0062] between a zero radius and the radius r₄ of the portion of said second buried slice having an index lower than the index of said cladding of the product of the radius by the index difference relative to said cladding is preferably less than or equal to 80×10⁻³ μm².

[0063] The value U₀₄ of twice the integral $\int_{0}^{r4}{\Delta \quad {{n(r)} \cdot \quad {\exp \left( \frac{- r^{2}}{b^{2}} \right)} \cdot r \cdot {r}}}$

[0064] between a zero radius and the radius r₄ of the portion of said second buried slice having an index lower than the index of said cladding of the product of the radius and the index difference relative to said cladding and the function exp(−r²/b²) where b=1.54 μm is preferably from 24.1×10⁻³ to 28.3×10⁻³ μm².

[0065] The value U₂₄ of twice the integral $\int_{r2}^{r4}{\Delta \quad {{n(r)} \cdot \quad {\exp \left( \frac{- r^{2}}{c^{2}} \right)} \cdot r \cdot {r}}}$

[0066] between the radius r₂ of the portion of said first buried slice having an index higher than the index of said cladding and the radius r₄ of the portion of said second buried slice having an index lower than the index of said cladding of the product of the radius and the index difference relative to the cladding and the function exp(−r²/c²) where c=4.67 μm is preferably from 9.8×10⁻³ to 42.6×10⁻³ μm².

[0067] The invention will be better understood and other features and advantages will become apparent in the light of the following description and the appended drawings, which are provided by way of example.

BRIEF DESCRIPTION OF THE DRAWINGS

[0068]FIG. 1 represents diagrammatically one example of a type of profile with four slices of a chromatic dispersion compensating optical fiber according to the invention.

[0069]FIG. 2 is a table comprising radius and index difference values for nine examples of profiles with three slices of a chromatic dispersion compensating optical fiber according to the invention.

[0070]FIG. 3 is a table comprising certain characteristics of the profiles of a chromatic dispersion compensating optical fiber according to the invention as defined in FIG. 2.

[0071]FIG. 4 is a table comprising other characteristics of the profiles of a chromatic dispersion compensating optical fiber according to the invention as defined in FIG. 2.

[0072]FIG. 5 is a table comprising radius and index difference values for eight examples of profiles with four slices of a chromatic dispersion compensating optical fiber according to the invention.

[0073]FIG. 6 is a table comprising certain characteristics of the profile of a chromatic dispersion compensating optical fiber according to the invention as defined in FIG. 5.

[0074]FIG. 7 is a table comprising other characteristics of the profiles of a chromatic dispersion compensating optical fiber according to the invention as defined in FIG. 5.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0075]FIG. 1 shows diagrammatically one example of a type of profile with four slices of a chromatic dispersion compensating optical fiber according to the invention. The first slice, or central slice as it is otherwise known, has a maximum index difference Δn1 relative to the constant index of the cladding and an outside radius r1. The maximum index difference Δn1 is positive. The index is preferably constant between a zero radius and the radius r1. The second slice, or first buried slice as it is otherwise known, has a maximum index difference Δn2 relative to the constant index of the cladding and an outside radius r2. The maximum index difference Δn2 is negative. The index is preferably constant between the radius r1 and the radius r2. The third slice, or annular slice as it is otherwise known, has a maximum index difference Δn3 relative to the constant index of the cladding and an outside radius r3. The maximum index difference Δn3 is positive. The index is preferably constant between the radius r2 and the radius r3. The fourth slice, or second buried slice as it is otherwise known, has a maximum index difference Δn4 relative to the constant index of the cladding and an outside radius r4. The maximum index difference Δn4 is negative. The index is preferably constant between the radius r3 and the radius r4. Beyond the radius r4 is the constant index cladding.

[0076]FIG. 1 also corresponds to an example of a type of profile with three slices of a chromatic dispersion compensating optical fiber according to the invention for which Δn4=0 and r4=r3. In this case, the second buried slice does not exist and the first buried slice is simply referred to as the buried slice.

[0077]FIG. 2 is a table comprising radius and index difference values for nine examples of profiles with three slices of a chromatic dispersion compensating optical fiber according to the invention. The left-hand column gives the number of the example from 1 to 9. The next three columns give in μm the radii of the core varying index profile. The last three columns give one thousand times the index differences (no units).

[0078]FIG. 3 is a table comprising certain characteristics of the profiles of a chromatic dispersion compensating optical fiber according to the invention as defined in FIG. 2. The left-hand column gives the number of the example from 1 to 9. For each example considered, the other columns give characteristics of the optical fiber corresponding to the example concerned. The next column gives the effective area S_(eff) expressed in μm² at the wavelength of 1 495 nm. The next column gives the chromatic dispersion C expressed in ps/nm.km at a wavelength of 1 495 nm. The next column gives the dispersion slope C′ expressed in ps/nm².km at a wavelength of 1 495 nm. The next column gives the chromatic dispersion C to dispersion slope C′ ratio expressed in nm at a wavelength of 1 495 nm. The next column gives the compensation in percent for the line optical fiber sold under the trademark “TERALIGHT ULTRA”. The next column gives the compensation in percent for the line optical fiber sold under the Trade Mark “TERALIGHT”. The next column gives the theoretical cut-off wavelength λ_(cth) expressed in nm. The last column gives the bending losses expressed in dB/m at the wavelength of 1 530 nm for winding to a radius of 10 mm.

[0079]FIG. 4 is a table comprising other characteristics of the profiles of a chromatic dispersion compensating optical fiber according to the invention as defined in FIG. 2. The left-hand column gives the numbers of the examples from 1 to 9. For each example considered, the other columns give characteristics of the optical fiber corresponding to the example concerned. The left-hand column also has entries MIN and MAX corresponding in the subsequent columns to a preferred minimum and a preferred maximum, respectively, for the value of the characteristic concerned. In each column, the first row comprising a numerical value corresponds to a preferred minimum value, the second row comprising a numerical value corresponds to a preferred maximum value, and the subsequent rows comprising numerical values correspond to real values for examples 1 to 9. The next column gives the value of S₀₁ expressed in thousandths of μm. The next column gives the value of T₀₁ expressed in thousandths of μm². The next column gives the value of S₁₂ expressed in thousandths of μm. The next column gives the value of T₁₂ expressed in thousandths of μm². The next column gives the value of S₂₃ expressed in thousandths of μm. The next column gives the value of T₂₃ expressed in thousandths of μm². The next column gives the value of S₂₃ expressed in thousandths of μm. The next column gives the value of T₀₃ expressed in thousandths of μm². The last column gives the value of U₀₃ expressed in thousandths of μm².

[0080]FIG. 5 is a table comprising the radius and index difference values for nine examples of profiles with four slices of a chromatic dispersion compensating optical fiber according to the invention. The left-hand column gives the numbers of the examples from 10 to 17. The next four columns give in μm the radii of the core varying index profile. The last four columns give one thousand times the index differences (no units).

[0081]FIG. 6 is a table comprising certain characteristics of the profiles of a chromatic dispersion compensating optical fiber according to the invention as defined in FIG. 5. Its description is analogous to that of FIG. 3.

[0082]FIG. 7 is a table comprising other characteristics of the profiles of a chromatic dispersion compensating optical fiber according to the invention as defined in FIG. 5. Its description is analogous to that of FIG. 4. 

1. An optical fiber with compensation of chromatic dispersion in the S band from 1 460 nm to 1 530 nm, for use in wavelength division multiplex transmission networks, having a negative chromatic dispersion at the wavelength of 1 495 nm, comprising successively from the center toward the periphery a core having a varying index profile and then a cladding of constant index, said varying index profile of said core comprising successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a buried slice having a minimum index lower than the index of said cladding, and an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, the difference between said maximum index of said central slice and the index of said cladding being from 11.5×10⁻³ to 20.0×10⁻³, the radius of the portion of said central slice having an index higher than the index of said cladding being from 1.6 μm to 2.6 μm, the value of the integral between a zero radius and the radius of the portion of said central slice having an index higher than the index of said cladding of the index difference relative to said cladding being from 28×10⁻³ μm to 34×10⁻³ μm, and the radii and the indices of each of said slices being determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to dispersion slope ratio whose absolute value is from 68 nm to 158 nm.
 2. The optical fiber claimed in claim 1 wherein the radii and the indices of each slice are determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 80 nm to 118 nm.
 3. The optical fiber claimed in claim 2 wherein the radii and the indices of each slice are determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 87 nm to 105 nm.
 4. The optical fiber claimed in claim 1 wherein the value of twice the integral between a zero radius and the radius of the portion of said central slice having an index higher than the index of said cladding of the product of the index difference relative to the cladding and the radius is from 51×10⁻³ μm² to 79×10⁻³ μm².
 5. The optical fiber claimed in claim 1 wherein the difference between the minimum index of said buried slice and the index of said cladding is from −10.0×10⁻³ to −7.0×10⁻³ and the outside radius of said buried slice is from 4.5 μm to 6.5 μm.
 6. The optical fiber claimed in claim 5 wherein the value of the integral between the radius of the portion of said central slice having an index higher than the index of said cladding and the radius of the portion of said buried slice having an index lower than the index of said cladding of the index difference relative to said cladding is from −42×10⁻³ to −22×10⁻³ μm.
 7. The optical fiber claimed in claim 6 wherein the value of twice the integral between the radius of the portion of said central slice having an index higher than the index of said cladding and the radius of the portion of said buried slice having an index lower than the index of said cladding of the product of the radius by the index difference relative to said cladding is from −350×10⁻³ to −160×10⁻³ μm².
 8. The optical fiber claimed in claim 1 wherein the difference between the maximum index of said annular slice and the index of said cladding is from 1.0×10⁻³ to 8.0×10⁻³ and the outside radius of said annular slice is from 7.3 μm to 10.2 μm.
 9. The optical fiber claimed in claim 8 wherein the value of the integral between the radius of the portion of said buried slice having an index lower than the index of said cladding and the radius of the portion of said annular slice having an index higher than the index of said cladding of the index difference relative to said cladding is from 5×10⁻³ to 15×10⁻³ μm.
 10. The optical fiber claimed in claim 9 wherein the value of twice the integral between the radius of the portion of said buried slice having an index lower than the index of said cladding and the radius of the portion of said annular slice having an index higher than the index of said cladding of the product of the radius by the index difference relative to said cladding is from 70×10⁻³ to 207×10⁻³ μm².
 11. The optical fiber claimed in claim 1 wherein the value of the integral between a zero radius and the radius of the portion of said annular slice having an index higher than the index of said cladding of the index difference relative to said cladding is from 2.8×10⁻³ to 18.2×10⁻³ μm.
 12. The optical fiber claimed in claim 11 wherein the value of twice the integral between a zero radius and the radius of the portion of said annular slice having an index higher than the index of said cladding of the product of the radius by the index difference relative to said cladding is from −108×10⁻³ to 57×10⁻³ μm².
 13. The optical fiber claimed in claim 12 wherein the value of twice the integral between a zero radius and the radius of the portion of said annular slice having an index higher than the index of said cladding of the product of the radius and the index difference relative to the cladding and the function exp(−r²/a²) where a=1.58 μm is from 24.4×10⁻³ to 28.5×10⁻³ μm².
 14. An optical fiber with compensation of chromatic dispersion in the S band from 1 460 nm to 1 530 nm, for use in wavelength division multiplex transmission networks, having a negative chromatic dispersion at the wavelength of 1 495 nm, comprising successively from the center toward the periphery a core having a varying index profile and then a cladding of constant index, said varying index profile of said core comprising successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a first buried slice having a minimum index lower than the index of said cladding, an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, a second buried slice having a minimum index lower than the index of said cladding, the radii and the indices of each of said slices being determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to dispersion slope ratio whose absolute value is from 68 nm to 158 nm.
 15. The optical fiber claimed in claim 14 wherein the radii and the indices of each slice are determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 80 nm to 118 nm.
 16. The optical fiber claimed in claim 15 wherein the radii and the indices of each slice are determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope whose absolute value is from 87 nm to 105 nm.
 17. The optical fiber claimed in claim 14 wherein the difference between the maximum index of said annular slice and the index of said cladding is from 12×10⁻³ to 20×10⁻³ and the radius of the portion of said central slice having an index higher than the index of said cladding is from 1.57 μm to 2.5 μm.
 18. The optical fiber claimed in claim 17 wherein the value of the integral between a zero radius and the radius of the portion of said central slice having an index higher than the index of said cladding of the index difference relative to said cladding is from 28.4×10⁻³ μm to 35.5×10⁻³ μm.
 19. The optical fiber claimed in claim 18 wherein the value of twice the integral between a zero radius and the radius of the portion of said central slice having an index higher than the index of said cladding of the product of the index difference relative to the cladding and the radius is from 49×10⁻³ μm² to 81×10⁻³ μm².
 20. The optical fiber claimed in claim 14 wherein the difference between the minimum index of said first buried slice and the index of said cladding is from −12×10⁻³ to −5×10⁻³ and the outside radius of said first buried slice is from 4.0 μm to 7.4 μm.
 21. The optical fiber claimed in claim 20 wherein the value of the integral between the radius of the portion of said central slice having an index higher than the index of said cladding and the radius of the portion of said first buried slice having an index lower than the index of said cladding of the index difference relative to said cladding is from −56×10⁻³ to −20×10⁻³ μm.
 22. The optical fiber claimed in claim 21 wherein the value of twice the integral between the radius of the portion of said central slice having an index higher than the index of said cladding and the radius of the portion of said first buried slice having an index lower than the index of said cladding of the product of the radius by the index difference relative to said cladding is from −470×10⁻³ to −130×10⁻³ μm².
 23. The optical fiber claimed in claim 14 wherein the difference between the maximum index of said annular slice and the index of said cladding is from 1.0×10⁻³ to 8.0×10⁻³ and the outside radius of said annular slice is from 6.8 μm to 12 μm.
 24. The optical fiber claimed in claim 23 wherein the value of the integral between the radius of the portion of said first buried slice having an index lower than the index of said cladding and the radius of the portion of said annular slice having an index higher than the index of said cladding of the index difference relative to said cladding is from 5×10⁻³ to 26×10⁻³ μm.
 25. The optical fiber claimed in claim 24 wherein the value of twice the integral between the radius of the portion of said first buried slice having an index lower than the index of said cladding and the radius of the portion of said annular slice having an index higher than the index of said cladding of the product of the radius by the index difference relative to said cladding is from 60×10⁻³ to 440×10⁻³ μm².
 26. The optical fiber claimed in claim 14 wherein the difference between the minimum index of said second buried slice and the index of said cladding is from −12×10⁻³ to 0 and the outside radius of said second buried slice is from 9 μm to 21 μm.
 27. The optical fiber claimed in claim 26 wherein the value of the integral between the radius of the portion of said annular slice having an index higher than the index of said cladding and the radius of the portion of said second buried slice having an index lower than the index of said cladding of the index difference relative to said cladding is from −153×10⁻³ μm to
 0. 28. The optical fiber claimed in claim 14 wherein the value of the integral between a zero radius and the radius of the portion of said second buried slice having an index lower than the index of said cladding of the index difference relative to said cladding is from −138×10⁻³ to 22×10⁻³ μm.
 29. The optical fiber claimed in claim 28 wherein the value of twice the integral between a zero radius and the radius of the portion of said second buried slice having an index lower than the index of said cladding of the product of the radius by the index difference relative to said cladding is less than or equal to 80×10⁻³ μm².
 30. The optical fiber claimed in claim 29 wherein the value of twice the integral between a zero radius and the radius of the portion of said second buried slice having an index lower than the index of said cladding of the product of the radius and the index difference relative to said cladding and the function exp(−r²/b²) where b=1.54 μm is from 24.1×10⁻³ to 28.3×10⁻³ m².
 31. The optical fiber claimed in claim 14 wherein the value of twice the integral between the radius of the portion of said first buried slice having an index higher than the index of said cladding and the radius of the portion of said second buried slice having an index lower than the index of said cladding of the product of the radius and the index difference relative to the cladding and the function exp(−r 2/c2) where c=4.67 μm is from 9.8×10⁻³ to 42.6×10⁻³ μm².
 32. An optical fiber with compensation of chromatic dispersion in the S band from 1 460 nm to 1 530 nm, for use in wavelength division multiplex transmission networks, having a negative chromatic dispersion at the wavelength of 1 495 nm, comprising successively from the center toward the periphery a core having a varying index profile and then a cladding of constant index, said varying index profile of said core comprising successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a buried slice having a minimum index lower than the index of said cladding, and an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, the absolute value of the minimum index of said buried slice being greater than or equal to 60% of the absolute value of the maximum index of said central slice.
 33. The optical fiber claimed in claim 32 wherein said varying index profile of said core comprises successively, from said center toward said periphery, a central slice having a maximum index higher than the index of said cladding, a first buried slice having a minimum index lower than the index of said cladding, an annular slice having a maximum index higher than the index of said cladding and lower than the maximum index of said central slice, and a second buried slice having an index lower than the index of said cladding.
 34. The optical fiber claimed in claim 32 wherein the radii and the indices of each slice are determined so that said dispersion compensating optical fiber has at the wavelength of 1 495 nm a chromatic dispersion to chromatic dispersion slope ratio whose absolute value is from 68 nm to 158 nm.
 35. An optical fiber claimed in claim 32 wherein the absolute value of the minimum index of said buried slice is greater than or equal to 90% of the absolute value of the maximum index of said central slice.
 36. An optical fiber transmission system comprising the combination of a line optical fiber and an optical fiber with chromatic dispersion compensation in the S band according to claim 1, wherein said dispersion compensating optical fiber is an in-line fiber.
 37. An optical fiber transmission system comprising the combination of a line optical fiber and an optical fiber with chromatic dispersion compensation in the S band according to claim 1, wherein said dispersion compensating optical fiber is an in-module fiber. 